Ceramics Wear Rate

The total wear rates of the cup and the head of ceramic on ceramic couples are about 35 fold lower than those of metal on metal.

Ceramics wear rate.

Ceramic on metal com bearings are considered to be a promising alternative to polyethylene based bearings or hard on hard bearings ceramic on ceramic coc and metal on metal mom. The wear rate per unit sliding distance in the transient wear regime decreases until it has reached a constant value in the steady state wear regime. The hip joint. The measured wear rates of various combinations of ceramic polyethylene and metal couples kaddick and pfaff 2002 are shown in table 7 2.

Arnell in tribology and dynamics of engine and powertrain 2010. The head wear rate alone is about 100 to 300 fold lower. The wear rate of al 2 o 3 13 tio 2 ceramic coating was evaluated by the wear volume and that of pins by weighing them before and after the tests. The friction and wear of oxide ceramics and silicon based ceramics in air at temperatures from room ambient to 900 c in a few cases to 1200 c were measured for a.

Although com shows lower wear rates than mom in vitro wear testing of com shows widely varying results. Identifying the run in and steady state wear rates was a valuable step in processing the ceramic wear data and assessing its reliability. The wear depth of pins was calculated by. Wear of ceramics and cermets.

Thus the m m and c c thrs have demonstrated two to three orders of reduction in volumetric wear in the laboratory compared with the pe wear standard which helps to explain the excellent wear performance and. Ceramics can exhibit very low wear rates compared with metals and they are being used increasingly in tribological situations they also retain similar properties up to high temperatures and they are very unreactive chemically so they will certainly find increasing use in hostile environments.